JIS H 2202:2016
JIS H 2202:2016 - Aluminium bronze
Notes
25 | Cu+Fe+Ni+Al+Mn 99.5% min. |
JIS H 2202:2016 - Bismuth brass
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>66 | - | - | - | 0.8 | 0.2 | - | - | 0.05 | - | 20 | - | - | 0.2 | - | - | - | - | - | |||
69 | 0.1 | 0.5 | 0.5 | 1.4 | 1 | - | - | 0.1 | 0.1 | 40 | - | - | 1.2 | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>66.3 | - | 1.1 | - | 0.01 | - | - | 0.06 | 0.05 | - | 20 | - | - | 0.5 | - | - | - | - | - | |||
68.5 | 0.1 | 1.5 | 0.2 | 0.1 | 0.2 | - | 0.15 | 0.1 | 0.05 | 40 | - | - | 0.8 | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>66 | - | 0.6 | - | 0.35 | - | - | 0.02 | - | 0.4 | 20 | - | - | 0.5 | - | - | - | - | - | |||
72 | 0.09 | 1.1 | 0.2 | 0.6 | 0.2 | 0.2 | 0.2 | 0.03 | 0.8 | 40 | - | - | 0.8 | - | - | - | - | - | ||||
JIS H 2202:2016 - Bismuth bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>86 | - | 4 | - | - | - | - | - | - | - | 4 | - | - | 0.4 | - | - | - | - | - | |||
90.6 | 0.1 | 6 | 0.3 | 0.005 | 0.8 | - | 0.3 | 0.03 | 0.005 | 8 | 0.05 | - | 1 | - | - | - | - | 0.1 | ||||
| //= ($i == 0) ? t("min") : t("max") ?>84.5 | - | 4 | - | - | - | - | - | - | - | 4 | - | - | 1 | - | - | - | - | - | |||
90 | 0.1 | 6 | 0.3 | 0.005 | 0.8 | - | 0.3 | 0.03 | 0.005 | 8 | 0.05 | - | 2.5 | - | - | - | - | 0.1 | ||||
| //= ($i == 0) ? t("min") : t("max") ?>83.5 | - | 4 | - | - | - | - | - | - | - | 4 | - | - | 2.5 | - | - | - | - | - | |||
88.5 | 0.1 | 6 | 0.3 | 0.005 | 0.8 | - | 0.3 | 0.03 | 0.005 | 8 | 0.05 | - | 3.5 | - | - | - | - | 0.1 | ||||
| //= ($i == 0) ? t("min") : t("max") ?>82.5 | - | 3 | - | - | 1.5 | - | - | - | - | 6 | - | - | 1 | - | - | - | - | - | |||
87.5 | 0.1 | 5 | 0.3 | 0.005 | 2.5 | - | 0.3 | 0.03 | 0.005 | 9 | 0.05 | - | 2 | - | - | - | - | 0.1 | ||||
| //= ($i == 0) ? t("min") : t("max") ?>80.1 | - | 1.5 | - | - | - | - | - | - | - | 12 | - | - | 0.4 | - | - | - | - | - | |||
85.1 | 0.1 | 3 | 0.3 | 0.005 | 0.5 | - | 0.05 | 0.03 | 0.005 | 17 | - | - | 0.9 | - | - | - | - | 0.1 | ||||
| //= ($i == 0) ? t("min") : t("max") ?>77.5 | - | 2 | - | - | - | - | - | - | - | 14 | - | - | 0.9 | - | - | - | - | - | |||
83 | 0.09 | 3 | 0.3 | 0.005 | 0.2 | - | 0.05 | 0.03 | 0.005 | 17 | - | - | 1.5 | - | - | - | - | 0.1 | ||||
Notes
27 | When the copper content is below the lower limit for Cu, the value may be added to the nickel content provided that Ni is within the specified limit, so Cu+Ni is reported |
28 | Cu+Sn+Zn+Bi+Ni 99.5% min. |
29 | Sn+Zn 19.0% max. |
JIS H 2202:2016 - Bismuth selenium bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>83 | - | 3.5 | - | - | - | - | - | - | - | 4 | - | - | 0.8 | - | - | - | - | 0.1 | |||
90.6 | 0.1 | 6 | 0.3 | 0.005 | 0.8 | - | 0.2 | 0.03 | 0.005 | 9 | 0.05 | - | 2.5 | - | - | - | - | 0.5 | ||||
Notes
27 | When the copper content is below the lower limit for Cu, the value may be added to the nickel content provided that Ni is within the specified limit, so Cu+Ni is reported |
JIS H 2202:2016 - Brass
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>83 | - | - | - | - | - | - | - | - | - | 10 | - | - | - | - | - | - | - | - | |||
88 | 0.5 | 0.1 | 0.2 | 0.2 | 0.2 | - | - | - | - | 20 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>65 | 0.5 | - | - | - | - | - | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
70 | 3 | 1 | 0.6 | 0.5 | 1 | - | - | - | - | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>58 | 0.5 | - | - | - | - | - | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
64 | 3 | 1 | 0.6 | 0.5 | 1 | - | - | - | - | 50 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>65.5 | 0.1 | 1.1 | - | 0.01 | - | - | 0.06 | 0.05 | - | 20 | - | - | - | - | - | - | - | - | |||
68.5 | 2 | 1.5 | 0.2 | 0.1 | 0.2 | - | 0.15 | 0.1 | 0.05 | 40 | - | - | - | - | - | - | - | - | ||||
JIS H 2202:2016 - Gun bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>79 | 3 | 2 | - | - | - | - | - | - | - | 8 | - | - | - | - | - | - | - | - | |||
83 | 7 | 4 | 0.35 | 0.005 | 0.8 | - | 0.2 | 0.03 | 0.005 | 12 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>86 | - | 7 | - | - | - | - | - | - | - | 3 | - | - | - | - | - | - | - | - | |||
90 | 1 | 9 | 0.2 | 0.005 | 0.8 | - | 0.2 | 0.03 | 0.005 | 5 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>83 | 4 | 4 | - | - | - | - | - | - | - | 4 | - | - | - | - | - | - | - | - | |||
87 | 6 | 6 | 0.3 | 0.005 | 0.8 | - | 0.2 | 0.03 | 0.005 | 6 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>86 | 1 | 5 | - | - | - | - | - | - | - | 3 | - | - | - | - | - | - | - | - | |||
90 | 3 | 7 | 0.2 | 0.005 | 0.8 | - | 0.2 | 0.03 | 0.005 | 5 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>84 | 2 | 4 | - | - | - | - | - | - | - | 5 | - | - | - | - | - | - | - | - | |||
88 | 4 | 6 | 0.3 | 0.005 | 0.8 | - | 0.2 | 0.03 | 0.005 | 7 | - | - | - | - | - | - | - | - | ||||
Notes
20 | Cu+Sn+Pb+Zn+Ni 99.0% min. |
21 | Cu+Sn+Zn+Ni 99.5% min. |
22 | Cu+Sn+Pb+Zn+Ni 99.5% min. |
27 | When the copper content is below the lower limit for Cu, the value may be added to the nickel content provided that Ni is within the specified limit, so Cu+Ni is reported |
JIS H 2202:2016 - High-lead tin bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>77 | 9 | 9 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
81 | 11 | 11 | 0.2 | 0.005 | 1 | - | 0.5 | 0.05 | 0.005 | 1 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>74 | 14 | 7 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
78 | 16 | 9 | 0.2 | 0.005 | 1 | - | 0.5 | 0.05 | 0.005 | 1 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>70 | 16 | 6 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
76 | 22 | 8 | 0.2 | 0.005 | 1 | - | 0.5 | 0.05 | 0.005 | 1 | - | - | - | - | - | - | - | - | ||||
Notes
24 | Cu+Sn+Pb+Ni 98.5% min. |
27 | When the copper content is below the lower limit for Cu, the value may be added to the nickel content provided that Ni is within the specified limit, so Cu+Ni is reported |
JIS H 2202:2016 - Leaded tin bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>82 | 4 | 9 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
86 | 6 | 11 | 0.2 | 0.005 | 1 | - | 0.3 | 0.05 | 0.005 | 1 | - | - | - | - | - | - | - | - | ||||
Notes
24 | Cu+Sn+Pb+Ni 98.5% min. |
27 | When the copper content is below the lower limit for Cu, the value may be added to the nickel content provided that Ni is within the specified limit, so Cu+Ni is reported |
JIS H 2202:2016 - Low-lead sulfur bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>90 | - | 3 | - | - | 0.1 | - | - | - | - | 1 | 0.2 | - | - | - | - | - | - | - | |||
96 | 0.1 | 5 | 0.3 | 0.005 | 1 | - | 0.2 | 0.05 | 0.005 | 3 | 0.6 | - | - | - | - | - | - | - | ||||
Notes
26 | Cu+Sn+Zn+Ni+S 99.5% min. |
JIS H 2202:2016 - Silicon brass
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>84 | - | - | - | - | - | - | - | - | 3.5 | 9 | - | - | - | - | - | - | - | - | |||
88 | 0.1 | - | - | 0.5 | - | - | - | - | 4.5 | 11 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>78.5 | - | - | - | - | - | - | - | - | 4 | 14 | - | - | - | - | - | - | - | - | |||
82.5 | 0.3 | - | - | 0.3 | - | - | - | - | 5 | 16 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>80 | - | - | - | - | - | - | - | - | 3.2 | 13 | - | - | - | - | - | - | - | - | |||
84 | 0.2 | - | 0.3 | 0.3 | - | 0.2 | - | - | 4.2 | 15 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>74 | - | - | - | - | - | - | - | 0.05 | 2.7 | 18 | - | - | - | - | - | - | - | - | |||
78 | 0.1 | 0.6 | 0.1 | - | 0.15 | 0.1 | 0.1 | 0.2 | 3.4 | 22.5 | - | - | 0.1 | - | - | - | - | 0.1 | ||||
JIS H 2202:2016 - Special brass
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>55 | - | - | 0.5 | 0.5 | - | 0.1 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
60 | 0.4 | 1 | 1.5 | 1.5 | 1 | 1.5 | - | - | 0.1 | 50 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>55 | - | - | 0.5 | 0.5 | - | 0.1 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
60 | 0.4 | 1 | 2 | 2 | 1 | 3.5 | - | - | 0.1 | 50 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>60 | - | - | 2 | 3 | - | 2.5 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
65 | 0.2 | 0.5 | 4 | 5 | 0.5 | 5 | - | - | 0.1 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>60 | - | - | 2 | 5 | - | 2.5 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
65 | 0.2 | 0.2 | 4 | 7.5 | 0.5 | 5 | - | - | 0.1 | 40 | - | - | - | - | - | - | - | - | ||||
JIS H 2202:2016 - Tin bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>86.5 | - | 9 | - | - | - | - | - | - | - | 1 | - | - | - | - | - | - | - | - | |||
89.5 | 1 | 11 | 0.2 | 0.005 | 0.8 | - | 0.2 | 0.03 | 0.005 | 3 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>87 | - | 9 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
91 | 0.3 | 12 | 0.2 | 0.005 | 0.5 | - | 0.05 | 0.1 | 0.005 | 0.3 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>84 | - | 12 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
88 | 0.3 | 15 | 0.2 | 0.005 | 0.5 | - | 0.05 | 0.1 | 0.005 | 0.3 | - | - | - | - | - | - | - | - | ||||
Notes
21 | Cu+Sn+Zn+Ni 99.5% min. |
23 | Cu+Sn+Ni+P 99.5% min. |
27 | When the copper content is below the lower limit for Cu, the value may be added to the nickel content provided that Ni is within the specified limit, so Cu+Ni is reported |